Iron(II) oxide

Iron(II) oxide
Iron(II) oxide
Names
IUPAC name
Iron(II) oxide
Other names
Ferrous oxide,iron monoxide
Identifiers
3D model (JSmol)
ChEBI
ChemSpider
ECHA InfoCard 100.014.292 Edit this at Wikidata
13590
UNII
  • InChI=1S/Fe.O checkY
    Key: UQSXHKLRYXJYBZ-UHFFFAOYSA-N checkY
  • InChI=1/Fe.O/rFeO/c1-2
    Key: UQSXHKLRYXJYBZ-WPTVXXAFAB
  • [Fe]=O
Properties
FeO
Molar mass 71.844 g/mol
Appearance black crystals
Density 5.745 g/cm3
Melting point 1,377 °C (2,511 °F; 1,650 K)
Boiling point 3,414 °C (6,177 °F; 3,687 K)
Insoluble
Solubility insoluble in alkali, alcohol
dissolves in acid
+7200·10−6 cm3/mol
2.23
Hazards
Occupational safety and health (OHS/OSH):
Main hazards
can be combustible under specific conditions
NFPA 704 (fire diamond)
NFPA 704 four-colored diamondHealth 1: Exposure would cause irritation but only minor residual injury. E.g. turpentineFlammability 1: Must be pre-heated before ignition can occur. Flash point over 93 °C (200 °F). E.g. canola oilInstability 0: Normally stable, even under fire exposure conditions, and is not reactive with water. E.g. liquid nitrogenSpecial hazards (white): no code
1
1
0
200 °C (392 °F; 473 K)
Safety data sheet (SDS) ICSC 0793
Related compounds
Other anions
Iron(II) sulfide
Iron(II) selenide
Iron(II) telluride
Other cations
Manganese(II) oxide
Cobalt(II) oxide
Related Iron oxides
Iron(II,III) oxide
Iron(III) oxide
Related compounds
Iron(II) fluoride
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
checkY verify (what is checkY☒N ?)
Infobox references

Iron(II) oxide or ferrous oxide is the inorganic compound with the formula FeO. Its mineral form is known as wüstite. One of several iron oxides, it is a black-colored powder that is sometimes confused with rust, the latter of which consists of hydrated iron(III) oxide (ferric oxide). Iron(II) oxide also refers to a family of related non-stoichiometric compounds, which are typically iron deficient with compositions ranging from Fe0.84O to Fe0.95O.

Preparation

FeO can be prepared by the thermal decomposition of iron(II) oxalate.

FeC2O4 → FeO + CO2 + CO

The procedure is conducted under an inert atmosphere to avoid the formation of iron(III) oxide (Fe2O3). A similar procedure can also be used for the synthesis of manganous oxide and stannous oxide.

Stoichiometric FeO can be prepared by heating Fe0.95O with metallic iron at 770 °C and 36 kbar.

Reactions

FeO is thermodynamically unstable below 575 °C, tending to disproportionate to metal and Fe3O4:

  • 4FeO → Fe + Fe3O4

Structure

Iron(II) oxide adopts the cubic, rock salt structure, where iron atoms are octahedrally coordinated by oxygen atoms and the oxygen atoms octahedrally coordinated by iron atoms. The non-stoichiometry occurs because of the ease of oxidation of FeII to FeIII effectively replacing a small portion of FeII with two-thirds their number of FeIII, which take up tetrahedral positions in the close packed oxide lattice.

In contrast to the crystalline solid, in the molten state iron atoms are coordinated by predominantly 4 or 5 oxygen atoms.

Below 200 K there is a minor change to the structure which changes the symmetry to rhombohedral and samples become antiferromagnetic.

Occurrence in nature

Iron(II) oxide makes up approximately 9% of the Earth's mantle. Within the mantle, it may be electrically conductive, which is a possible explanation for perturbations in Earth's rotation not accounted for by accepted models of the mantle's properties.

Uses

Iron(II) oxide is used as a pigment. It is FDA-approved for use in cosmetics and it is used in some tattoo inks. It can also be used as a phosphate remover from home aquaria.

See also


This page was last updated at 2024-03-17 02:39 UTC. Update now. View original page.

All our content comes from Wikipedia and under the Creative Commons Attribution-ShareAlike License.


Top

If mathematical, chemical, physical and other formulas are not displayed correctly on this page, please useFirefox or Safari